Green Mold Compound

Moldability and Reliability in Wire Bonded Packages

BY T. Y. LIN AND C.M. FANG

With the electronics industry driving for cost reduction, miniaturization and functional integration, the conventional integrated circuit (IC) package design is forced to migrate to finer wire bonding pad pitches, from 90 to 60 µm, or even 35 µm staggered pitch. Glob-top dispensing and central gate molding are innovative methods for achieving high-assembly yield.

For these alternative methods to transfer molding, the concurrent fine-tuning of mold compound viscosity and process parameter optimization are required. The ongoing trend for high-density wire bonds dictates not only a smaller bonding pad pitch, but the wire itself also is becoming thinner. Filler contents of the mold compound are increased gradually to reduce the coefficient of thermal expansion (CTE) and improve package strength.


Figure 1. Wire sweep is defined as the maximum wire deformation expressed as a percentage of the wire loop length.
Click here to enlarge image

null

The green mold compound used for high-density wire bonded packages often is highly moisture resistant, which can prevent the occurrence of “popcorn” failures in the plastic IC packages.

In this study, both moldability and reliability were assessed in terms of wire sweep, mold void, coplanarity performance and temperature cycle results. Wire sweep issues were improved greatly, but coplanarity still needs to be improved due to relatively high warpage problems. Although the traditional popcorn failures were not observed, new failure modes were found after 500 temperature cycles (temperature range from -55° to 150°C) with moisture soaking at MSL3.

Test Vehicle Selection

Transfer molding is an automatic compression molding process where the mold compounds are preheated and then transferred into the mold cavities. Generally, transfer molding is applied for chip-up types of packages, and gold wires at the corner adjacent to the mold gate show maximum sweep depending on force and speed. The bond pitch and wire span as well as the bonding strength could be the critical factors influencing wire sweep under a certain level of flow velocity, viscosity, etc. Wire bond loop height, as well as wire diameter and stiffness also impact the performance of wire sweep. In this study, a 216-lead thin quad flat pack (TQFP) was selected as the test vehicle.

The objective of the moldability studies was to assess the suitability of the evaluated compound for mass production. Additionally the process window was assessed and batch-to-batch, lot-to-lot variations of the mold compound were evaluated. The moldability studies focus on the evaluations of wire sweep, lead frame paddle tilt, mold voids and coplanarity.

Three green mold compounds (GMC-1, -2 and -3) were evaluated. GMC-1 was the original green compound for evaluation, and its wire sweep was 5 to 8 percent, more than the 4 percent that was specified as the internal wire sweep limit. Wire sweep is defined as the ratio of the maximum wire deviation (deformation) to the wire span. The wire sweep for molding temperatures in the range of 170° to 190°C were above 4 percent, which indicates that no process window was found for GMC-1. Following that, GMC-2 was formulated after fine-tuning the viscosity. The performance of wire sweep was improved, but coplanarity could not achieve the target for production. GMC-3 was then formulated by changing the catalyst type and fine-tuning the viscosity. The performance of wire sweep on GMC-3 was almost the same as GMC-2, and the coplanarity of GMC-3 passed the requirements of production. The warpage and coplanarity for GMC-3 were better at a molding temperature of 170°C than 180° or 190°C. This result indicates that the process window was not large.

Click here to enlarge image

null

Click here to enlarge image

null

Click here to enlarge image

null

Click here to enlarge image

null

Click here to enlarge image

null

Click here to enlarge image

null

Click here to enlarge image

null

Reliability Assessment

Typically, the major parts of a reliability evaluation include autoclave, temperature shock (liquid-to-liquid -55° to 125°C), temperature cycling (TC), high temperature storage, and temperature and humidity with bias. In this study, only the main TC results based on JEDEC condition C (-65° to 150°C) were reported because several failure modes were observed during the TC tests.


Figure 2. Mold body warpage measured by co-planarity scanner (molding at 170

POST A COMMENT